Characteristics on Treated Kenaf Fiber Reinforced Polypropylene Composites

What is it about?

Nowadays natural fiber and polymer matrix are being extensively used as alternatives in producing furniture like ceiling, floor and etc. to fulfill society demand instead of environmental friendly and saving cost. The objective of this study is to investigate the effects of maleic anhydride grafted polypropylene (MAPP) as a coupling agent for reinforcement between kenaf fiber (KF) and polypropylene (PP). The ratio of MAPP between 3% and 5% was observed to determine which composition ratio is better. The tensile strength for both 30% KF and 40% KF was treated through the alkali treatment process with 5% sodium hydroxide (NaOH). Kenaf fiber reinforced polypropylene (PP/KF) composites were melt blended and then used hydraulic molding test press machine for characterization to observe their tensile strengths by measuring their threshold. Tensile test was carried out to determine the tensile stresses of the composite at the best composition ratio of kenaf fiber that are 30% KF and 40% KF instead of MAPP ratio. The result shows 40% KF (5% MAPP) lead to better tensile performance compared to 40% KF (3% MAPP), 30% KF (5% MAPP) and 30% KF (3% MAPP). Meanwhile, Scanning electron microscopy (SEM) is used to observe the morphological comparison between untreated KF and treated KF as well as PP/KF. The good interfacial bonding between KF and PP was 5% MAPP rather than 3% MAPP due to the optimum strength received. Overall 5% MAPP with 40% PP/KF had shown the best result compared to others with the estimated tensile strength value of 21.38 MPa.

Featured Image

Why is it important?

To produce wood polymer composites in terms of reducing cost and increased of quality,

Perspectives