Semiconductor Heterojunctions for Enhanced Visible Light Photocatalytic H2 Production

What is it about?

Semiconductor-based heterojunctions have been shown to be effective photocatalytic materials to overcome the drawbacks of low photocatalytic efficiency that results from a high rate of electron−hole recombination and narrow photo-response range. In this paper, we report on the study of heterojunctions made from visible light active, graphitic carbon nitride, g-C3N4), and UV light active, strontium pyroniobate, Sr2Nb2O7. Heterojunctions made from a combination of g-C3N4 and nitrogen-doped Sr2Nb2O7 obtained at different temperatures were also studied to determine the effect of N doping. The photocatalytic performance was evaluated by using photocatalytic hydrogen evolution reaction (HER)from water g under visible light irradiation. It was found that the photocatalytic activities of as prepared heterojunctions are significantly higher than that of individual components under similar conditions. Heterojunction formed from g-C3N4 and N-doped Sr2Nb2O7 at 700oC (CN/SNON-700) showed better performance than heterojunction made from g-C3N4 and Sr2Nb2O7 (CN/SNO). A plausible mechanism for the heterojunction enhanced photocatalytic activity is proposed based on, relative band positions, and photoluminescence data.

Featured Image

Why is it important?

This study compares the photocatalytic activities of two different types of heterojunctions.