Peak broadening anisotropy in deformed face-centred cubic and hexagonal close-packed alloys

T. H. Simm, P. J. Withers, J. Quinta da Fonseca
  • Journal of Applied Crystallography, August 2014, International Union of Crystallography
  • DOI: 10.1107/s1600576714015751

Or how diffraction peaks can broaden based on dislocation types as much as dislocation density

What is it about?

On how diffraction peak profile analysis can be used with polycrystal plasticity models (in this case Taylor and Sachs models). We also show how dislocation structures, from alloys with different stacking fault energy, influence this relationship.