Ablation-resistant carbide Zr0.8Ti0.2C0.74B0.26 for oxidizing environments up to 3,000 °C

Yi Zeng, Dini Wang, Xiang Xiong, Xun Zhang, Philip J. Withers, Wei Sun, Matthew Smith, Mingwen Bai, Ping Xiao
  • Nature Communications, June 2017, Springer Science + Business Media
  • DOI: 10.1038/ncomms15836