What is it about?
Magnetoelectric (NixCo1-xFe2O4)0.3-(SryBa1-yNb2O6)0.7 composites with a 0–3 connectivity and different cation stoichiometries were synthesized via a classical mixed-oxide method. XRD patterns of all ceramics show reflections of the target phases SryBa1-yNb2O6 and NixCo1-xFe2O4. The influence of stoichiometry of the ferrimagnetic and ferroelectric phase on the magnetoelectric behavior was studied on composites with composition of (NixCo1-xFe2O4)0.3-(Sr0.5Ba0.5Nb2O6)0.7 and (NiFe2O4)0.3-(SryBa1-yNb2O6)0.7. The magnetic Curie temperature increases with nickel content. However, the saturation magnetizations as well as the Curie temperatures of the composites are always lower than the ones of bulk NixCo1-xFe2O4 samples. The maximum magnetoelectric coefficient (αME) rises with increasing nickel content from 40 (x = 0) to 180 μV Oe-1 cm-1 (x = 1) in accordance with the dynamic magnetostriction coefficient. The evolution of αME of (NiFe2O4)0.3-(SryBa1-yNb2O6)0.7 composites shows an increase with strontium content up to y 0.5. Higher strontium content leads to a significant reducing of αME.
Featured Image
Photo by Hal Gatewood on Unsplash
Why is it important?
The paper shows the influence of the cation stoichiometry on the magnetoelectric output
Read the Original
This page is a summary of: Magnetoelectric, dielectric, and magnetic investigations of multiferroic NixCo1−xFe2O4−SryBa1−yNb2O6 composites, Materials Research Bulletin, September 2024, Elsevier,
DOI: 10.1016/j.materresbull.2024.112860.
You can read the full text:
Resources
Contributors
The following have contributed to this page