Shrinkage mechanism and phase evolution of nanometer BaTiO3 powder containing 10mol% BaGeO3

What is it about?

Paper: https://www.researchgate.net/publication/232042038_Shrinkage_mechanism_and_phase_evolution_of_fine-grain_BaTiO3_powder_compacts_containing_10_mol_BaGeO3_prepared_via_a_precursor_route Abstract: The shrinkage mechanism of BaTiO3 powder compacts containing 10 mol% BaGeO3, synthesized by a precursor route and a conventional mixed-oxidemethod, are described herein. The calcination of a barium titanium germanium 1,2-ethanediolato complex precursor – [Ba(HOC2H4OH)4][Ti0.9Ge0.1(OC2H4O)3] (1) – at 730°C leads to a nm-sized Ba(Ti0.9/Ge0.1)O3 powder (1a) (SBET = 16.9 m2 g−1) consisting of BaTiO3 and BaGeO3. Whereas the conventional mixed-oxide method yields a powder (2) with a specific surface area of SBET = 2.0 m2 g−1. Powder compacts of 1a start to shrink at 790 °C and the shrinkage rate reaches a maximum at 908 °C. Dense ceramic bodies can be obtained below the appearance of the liquid melt (1120 °C), therefore the shrinkage of 1a can be described by a solid state sintering mechanism. Otherwise the beginning of the shrinkage of powder 2 is shifted to higher temperatures and the formation of the liquid melt is necessary to obtain dense ceramic bodies. Isothermal dilatometric investigations indicate that the initial stage of sintering is dominated by sliding processes. XRD investigations showthat belowa sintering temperature of 1200 °C ceramic bodies of 1a consist of tetragonal BaTiO3 and hexagonal BaGeO3, whereas temperatures above 1200 °C lead to ceramics containing orthorhombic BaGeO3, and a temperature of 1350 °C causes the formation of a Ba2TiGe2O8 phase. The phase evolution of ceramic bodies of 2 is similar to 1a, however a Ba2GeO4 phase is observed below a temperature of 1100 °C.

Featured Image